Physical and Electrochemical Effect of Bimetallic Pd-Mo Nanoalloys Supported on Vulcan XC-72R Carbon as Cathode Catalysts for Proton Exchange Membrane Fuel Cell

Basit Öğe Kaydı
dc.authoridAKDAG, ABDURRAHMAN/0000-0001-5292-8001
dc.contributor.authorSahin, Omer
dc.contributor.authorAkdag, Abdurrahman
dc.contributor.authorHoroz, Sabit
dc.contributor.authorEkinci, Arzu
dc.date.accessioned2024-12-24T19:25:04Z
dc.date.available2024-12-24T19:25:04Z
dc.date.issued2023
dc.departmentSiirt Üniversitesi
dc.description.abstractSynthesis of the bimetallic carbon-supported Pd and PdMo electrocatalysts via the chemical reduction with sodium borohydride as a reducing agent is presented. The Pd/C and PdMo/C electrocatalysts were used as cathode electrocatalysts in proton exchange membrane (PEM) fuel cells in order to examine their catalytic activity. The characterization of the prepared nanoparticles has been carried out using various methods, including X-ray diffraction (XRD), scanning electron microscopy (SEM), and energy- dispersive X-ray analysis (EDX). Moreover, the activities of the produced catalysts have been determined using cyclic voltammetry (CV), chronoamperometry, electrochemical impedance spectroscopy (EIS), and single-cell PEM fuel cell. The findings reveal that the crystallite size of the electrocatalysts Pd and Pd-Mo is less than 5.5 nm and that the Pd-Mo/C catalyst exhibits high activity for the oxygen reduction process when used alone. Furthermore, catalysts outperform other temperatures at 70 degrees C under varied cell temperatures and Mo concentrations in a single-cell fuel cell. A single cell using Pd-Mo/C as the cathode achieves a maximum power density of 107 mW cm(-2) at its maximum current density. Maximum current densities of synthesized catalysts at 70 degrees C cell temperature were measured as 61, 116, 188, and 168 mA cm(-2) for Pd/C, PdMo/C, PdMo2/C, and PdMo3/C catalysts, respectively. The efficiency according to the current of the PdMo2/C cathode catalyst at 70 degrees C was 52%, and Pd/C, PdMo/C, and PdMo3/C cathode catalysts at the same temperature were calculated as 26%, 38%, and 50%, respectively. The evenly scattered nanoparticles and more crystalline lattice flaws in the Pd-Mo/C catalyst are thought to be responsible for the catalyst's superior performance.
dc.description.sponsorshipResearch Foundation of Siirt University [2021-SIUSBF-10]
dc.description.sponsorshipThe authors would like to express their gratitude to the Research Foundation of Siirt University for providing financial assistance via project 2021-SIUSBF-10.
dc.identifier.doi10.1007/s12678-022-00787-7
dc.identifier.endpage212
dc.identifier.issn1868-2529
dc.identifier.issn1868-5994
dc.identifier.issue2
dc.identifier.scopus2-s2.0-85140581655
dc.identifier.scopusqualityQ2
dc.identifier.startpage202
dc.identifier.urihttps://doi.org/10.1007/s12678-022-00787-7
dc.identifier.urihttps://hdl.handle.net/20.500.12604/6228
dc.identifier.volume14
dc.identifier.wosWOS:000874414800001
dc.identifier.wosqualityQ3
dc.indekslendigikaynakWeb of Science
dc.indekslendigikaynakScopus
dc.language.isoen
dc.publisherSpringer
dc.relation.ispartofElectrocatalysis
dc.relation.publicationcategoryMakale - Uluslararası Hakemli Dergi - Kurum Öğretim Elemanı
dc.rightsinfo:eu-repo/semantics/closedAccess
dc.snmzKA_20241222
dc.subjectProton exchange membrane fuel cells
dc.subjectPalladium molybdenum catalyst
dc.subjectOxygen reduction reaction
dc.subjectElectro catalyst
dc.titlePhysical and Electrochemical Effect of Bimetallic Pd-Mo Nanoalloys Supported on Vulcan XC-72R Carbon as Cathode Catalysts for Proton Exchange Membrane Fuel Cell
dc.typeArticle

Dosyalar

Koleksiyon

WOS İndeksli Yayınlar Koleksiyonu
Scopus İndeksli Yayınlar Koleksiyonu