Multi-step heating strategy during thermal stabilization of polyacrylonitrile multi-filament bundle before carbonization

Basit Öğe Kaydı
dc.authoridTUNCEL, Kemal Sahin/0000-0001-5095-6543
dc.authoridHARIRI, HIBA/0000-0001-6396-1966
dc.contributor.authorHariri, Hiba
dc.contributor.authorTuncel, Kemal Sahin
dc.contributor.authorKaracan, Ismail
dc.date.accessioned2024-12-24T19:24:21Z
dc.date.available2024-12-24T19:24:21Z
dc.date.issued2024
dc.departmentSiirt Üniversitesi
dc.description.abstractA polyacrylonitrile (PAN) multi-filament bundle underwent a multi-step heat treatment following impregnation with a solution of ammonium bromide, phosphoric acid and urea (A-P-U). The multi-step thermal stabilization process was conducted in an air atmosphere at temperatures ranging from 200 to 245 degrees C for various stabilization times spanning from 10 to 70 min. Comprehensive analysis of physical and mechanical properties, infrared (IR) spectroscopy, X-ray diffraction (XRD) and thermal analysis (DSC and TGA) revealed the significant influence of stabilization time on the structure and properties of thermally stabilized PAN multi-filament bundle. The fiber thickness and linear density of the stabilized fibers decreased by approximately 29.5% and 10.6%, respectively, after 70 min of heat treatment. However, the fiber density value increased from 1.18 to 1.38 g cm(-3) during the same stabilization time. Additionally, the carbon yield value obtained using TGA increased from 31% to 73% at 850 degrees C. The presence of A-P-U markedly reduced the time needed for the conversion of the PAN polymer into a cyclized structure through its nitrile groups, thereby accelerating the stabilization reactions. Furthermore, the IR spectra exhibited the appearance of C=C bonds, signaling the creation of a crosslinked ladder-like structure. The XRD traces confirmed the decrease in crystallinity with increasing stabilization time, consistent with the findings from IR spectra. The findings showed that the A-P-U integrated system is notably successful and proficient in promoting the cyclization of nitrile groups, thereby decreasing the time needed to establish a thermally stable structure capable of withstanding elevated carbonization temperatures. (c) 2024 The Author(s). Polymer International published by John Wiley & Sons Ltd on behalf of Society of Chemical Industry.
dc.description.sponsorshipScientific and Technological Research Council of Turkiye (TUBITAK)
dc.description.sponsorshipThe assistance and cooperation of AKSA Akrilik AS (Turkey) are gratefully acknowledged for providing the PAN precursor filaments. Open access funding provided by the Scientific and Technological Research Council of Turkiye (TUBITAK).
dc.identifier.doi10.1002/pi.6665
dc.identifier.endpage832
dc.identifier.issn0959-8103
dc.identifier.issn1097-0126
dc.identifier.issue10
dc.identifier.scopus2-s2.0-85194385655
dc.identifier.scopusqualityQ1
dc.identifier.startpage824
dc.identifier.urihttps://doi.org/10.1002/pi.6665
dc.identifier.urihttps://hdl.handle.net/20.500.12604/5929
dc.identifier.volume73
dc.identifier.wosWOS:001230336100001
dc.identifier.wosqualityN/A
dc.indekslendigikaynakWeb of Science
dc.indekslendigikaynakScopus
dc.language.isoen
dc.publisherWiley
dc.relation.ispartofPolymer International
dc.relation.publicationcategoryMakale - Uluslararası Hakemli Dergi - Kurum Öğretim Elemanı
dc.rightsinfo:eu-repo/semantics/openAccess
dc.snmzKA_20241222
dc.subjectcarbon fiber
dc.subjectinfrared spectroscopy
dc.subjectpolyacrylonitrile
dc.subjectthermal stabilization
dc.subjectX-ray diffraction
dc.titleMulti-step heating strategy during thermal stabilization of polyacrylonitrile multi-filament bundle before carbonization
dc.typeArticle

Dosyalar

Koleksiyon

WOS İndeksli Yayınlar Koleksiyonu
Scopus İndeksli Yayınlar Koleksiyonu