Özet

The study of physicochemical properties of nano-ZrO2+3mol.%Y2O3 was determined. The X-ray diffraction spectrum of the nano-ZrO2 and system nano-ZrO2+3 mol.%Y2O3 compound was drawn by the Ritveld method and the crystal structure was determined at different temperatures (T = 373, 473, 573, 673 K) and under normal conditions. The energy of the arrangement of H2 as a result of the decay of H2O, on the surface of nano-ZrO2+3mol.%Y2O3 was considered. Impacts of adsorption and desorption preparation of ZrO2+3mol.%Y2O3 nanoparticles were considered at diverse (T = 373, 473, 573, 673 K) temperatures. The thought of H2 in warm forms at nano-ZrO2+3mol.%Y2O3 framework expanded. This tells about hydrogen era by water part in close future. Nano-ZrO2 and system nano-ZrO2+3mol.%Y2O3 with the temperature range of T = 373, 473, 573, 673 K have been studied by SEM analysis. These results are promising of hydrogen generation by water splitting in near future. © 2023, Walailak University. All rights reserved.

Açıklama

Anahtar Kelimeler

Adsorption, desorption, Hydrogen generation, Kinetics, Nano-ZrO<sub>2</sub>+3mol.%Y<sub>2</sub>O<sub>3</sub>, Thermal processes

Kaynak

Trends in Sciences

WoS Q Değeri

Scopus Q Değeri

Q3

Cilt

20

Sayı

4

Künye