    Öğe
    Fe doped-CoB catalysts with phosphoric acid-activated montmorillonite as support for efficient hydrogen production via NaBH4 hydrolysis
    (Pergamon-Elsevier Science Ltd, 2021) Balbay, Asim; Selvitepe, Nuran; Saka, Cafer
    In this study, montmorillonite (MMT) clay was modified with different acids to be used as support material. The modified MMT clay was used to obtain hydrogen in the hydrolysis reactions of NaBH4 (NaBH4-HR) as a support material for the Co-B and Co-Fe-B catalyst. During the activation of MMT clay, the effects of different acids, phosphoric acid (H3PO4) concentration, and impregnation time with H3PO4 were investigated. During the hydrogen generation from the NaBH4-HR, effects of Co loading, Fe loading, NaBH4 concentration, temperature and, catalyst durability were investigated. The maximum HGRs for MMT-H3PO4-CoB and MMT-H3PO4-CoeFeeB treated with 5 M H3PO4 for 7 days were 1869 and 4536 mL/min/gcatalyst, respectively. The activation energies for MMT-H3PO4-CoB and MMT-H3PO4-Co-Fe-B catalyst samples were 49.5 and 38.90 kJ/mol. (C) 2020 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.
  • Küçük Resim
    Öğe
    Optimisation of sepiolite clay with phosphoric acid treatment as support material for CoB catalyst and application to produce hydrogen from the NaBH4 hydrolysis
    (Elsevier-Hydrogen energy, 2019) Selvitepe, Nuran; Balbay, Asım; Saka, Cafer
    Herein, the CoB catalyst supported on the sepiolite clay treated with phosphoric acid was utilized to produce hydrogen from the NaBH4 hydrolysis. In order to analyse the performance of the phosphoric acid treated sepiolite clay supported-CoB catalyst, the NaBH4 concentration effect, phosphoric acid concentration effect, phosphoric acid impregnation time effect, CoB catalyst percentage effect, and temperature effect were studied. In addition, XRD, XPS, SEM, TEM, BET, and FTIR analysis were performed for characterization of CoeB catalyst supported on the acid-treated sepiolite. The completion time of this hydrolysis reaction with CoeB (20%) catalyst supported on the sepiolite treated by 5 M phosphoric acid was approximately 80 min, whereas the completion time of this hydrolysis reaction with acid-free sepiolite-supported CoeB (20%) catalyst was approximately 260 min. There is a five-fold increase in the maximum production rate. The maximum hydrogen production rates of this hydrolysis reaction at 30 and 60 C were found as 1486 and 5025 ml min 1g 1 catalyst, respectively. Activation energy was found as 21.4 kJ/mol. This result indicates that the acid treatment on sepiolite is quite successful. The re-usability of NaBH4 hydrolysis reaction by CoB catalyst supported on sepiolite treated phosphoric acid for successive five cycles of NaBH4 at 30 C was investigated.
  • [ X ]
    Öğe
    Sodyum bor hidrürlü bir hidrojen üretim sisteminde farklı kil bazlı katalizörlerin hidrojen üretimine etkileri
    (Siirt Üniversitesi, 2019) Selvitepe, Nuran; Balbay, Asım
    Bu çalışmada, destek malzemesi olarak farklı asitlerle modifiye edilmiş sepiyolit ve montmorillonit killeri üzerine Co-B, Co-Fe-B ve Co-Mg-B katalizörleri kimyasal indirgenme yöntemi ile sentezlenmiş ve aktiviteleri sodyum bor hidrürün hidroliz reaksiyonundan hidrojen elde etme ile gerçekleştirilmiştir. Sepiyolit ve montmorillonit killerinin modifikasyonu için asetik asit, hidroklorik asit, borik asit ve fosforık asit kullanılmıştır. Aynı zamanda, kil numunelerinin optimizasyonu için optimum asit konsantrasyonu ve optimum emdirme süreleri belirlenmiştir. Hidrojen üretim deneylerinde, metal miktarı, sodyum borhidrür konsantrasyonu ve sıcaklık parametreleri incelenmiştir. Her iki destek materyali ile asitlerin etkileşimi farklı olmakla birlikte en uygun hidrojen üretim hızları fosforik asitle elde edilmiştir. Aynı zamanda, destek materyali üzerine Co metali yanında Mg ya da Fe metal ilavesi ile de maksimum hidrojen üretiminde artışlar tespit edilmiştir. Gerçekleştirilen işlemler sonucunda elde edilen destekli katalizör numuneleri, X-ışınları kırınımı spektroskopisi (XRD), taramalı elektron mikroskobu, infrared spektroskopisi ve BET yüzey alanı cihazı ile karakterize edilmiş ve yorumlanmıştır. Karakterizasyon çalışmalarında, destekli katalizörlerin yüzeyinde anlamlı değişiklikler gözlemlenmiştir. Seçilen bazı katalizörler üzerinde, kinetik verilerin elde edilebilmesi için 30, 40, 50 ve 60 °C sıcaklıklarında hidroliz işlemleri gerçekleştirilmiştir. Kil destekli katalizörler kullanılarak sodyum borhidrürün hidrolizinden hidrojen üretimine ait aktivasyon enerjileri hesaplanmıştır. Montmorillonit destekli Co-B, Co-Fe-B ve Co-Mg-B katalizörleri ile elde edilen aktivasyon enerjileri sırasıyla 49.5, 38.90 ve 52.3 kJ/mol olarak bulunmuştur. Aynı zamanda, sepiyolit destekli Co-B, Co-Fe-B ve Co-Mg-B katalizörleri ile elde edilen aktivasyon enerjileri sırasıyla 21.4, 43.83 ve 38.21 kJ/mol olarak bulunmuştur. Anahtar Kelimeler: Co-B, Co-Fe-B. Co-Mg-B, destek materyal, hidrojen, modifikasyon